船用錨鏈圓鋼(YB/T66-1987)
(1)尺寸規格見表1。
表1船用錨鏈圓鋼的尺寸規格
| 圓鋼直徑d/mm | 理論質量/(kg/m) | 允許偏差/mm | 圓鋼直徑d/mm | 理論質量/(kg/m) | 允許偏差/mm |
| 13 | 1.04 | ±0.35 | 62* | 23.7 | ±0.70 |
| 14.5 | 1.30 | 64* | 25.25 | ||
| 17 | 1.78 | 66* | 28.86 | ||
| 18 | 2.00 | 68* | 28.5 | ||
| 20 | 2.47 | 70* | 30.2 | ||
| 2l | 2.72 | ±O.50 | 72* | 31.96 | |
| 22 | 2.98 | 75* | 34.7 | ||
| 23* | 3.26 | 78* | 37.51 | ||
| 25 | 3.85 | 80* | 29.5 | ||
| 27* | 4.49 | 83* | 42.47 | ±1.O | |
| 29* | 5.18 | 86* | 45.6 | ||
| 32 | 6.13 | 89* | 48.84 | ||
| 34 | 7.13 | 92 | 52.18 | ||
| 36 | 7.99 | 94* | 54.48 | ||
| 38 | 8.92 | 97* | 58.01 | ||
| 40 | 9.86 | 99* | 60.43 | ||
| 42 | 10.90 | 102* | 64.14 | ||
| 44* | 11.94 | 105 | 68.O | ||
| 46* | 13.05 | 108* | 71.91 | ||
| 48 | 14.2 | 110 | 74.6 | ||
| 50 | 15.4 | 114* | 80.13 | ±1.3 | |
| 52* | 16.67 | ±O.70 | 117* | 84.4 | |
| 54* | 17.98 | 120 | 88.8 | ||
| 56* | 19.3 | 120 | 96.3 | ||
| 58* | 20.7 | 130 | 104 | ||
| 60* | 22.2 |
注：帶*號者為圓鋼直徑的補充系列。
(2)牌號和化學成分見表2。
表2船用錨鏈圓鋼的牌號和化學成分
| 強度等級 | 牌號 | 化學成分(質量分數)(%) | ||||
| C | Mn | Si | - | - | ||
| ≤ | ||||||
| l | M15 | ≤O.18 | O.40～0.60 | ≤O.05 | O.040 | 0.040 |
| 2 | M20Mn | ≤O.24 | 1.10～1.60 | O.20～O.55 | O.040 | O.040 |
| 3 | M30Mn2 | ≤O.36 | 1.30～1.80 | O.20～O.55 | 0.040 | 0.040 |
表3船用錨鏈圓鋼的力學性能
| 強度等級 | 牌號 | 力學性能 | 冷彎試驗a=試樣直徑d=彎心直徑 | 試樣狀態 | ||||
| 拉力試驗 | 沖擊試驗 | |||||||
| 抗拉強度ób/MPa | 伸長率δ5(%) | 斷面收縮率ψ(%) | V型缺口沖擊韌度/(J/cm2) | |||||
| 試驗溫度 | 三個試驗平均值 | |||||||
| 1 | M15 | ≥345 | ≥30 | - | - | - | 180°d=a | 熱軋 |
| 2 | M20Mn | 490～690 | ≥22 | - | - | - | - | 熱軋 |
| 3 | M30Mn2 | ≥690 | ≥17 | ≥40 | 0℃ | 59 | 180°d=1.5a | 熱處理 |